Tungsten Alloy Swaging Rod for Military

Tungsten Alloy Military Swaging Rod

Swaging greatly increases tungsten alloy rod's ultimate tensile strength. The ultimate tensile strength of regular tungsten alloy rod is 1050 MPa . However, after swaging, the ultimate tensile strength can reach 1200 MPa min, we can even control tungsten alloy military swaging rod at 1400 MPa. Tungsten alloy military swaging rod is one of our main products. The composition of tungsten alloy military swaging rod is 93%WNiFe. Our common types:
Diameter: 12mm~20mm, Length: less than 400mm;
Diameter: 20mm~400mm, Length: less than 500mm.
We can manufacture other products according to customers' specific requirements.

Tungsten Alloy Military Swaging Rod Pictures

Tungsten Alloy Military Swaging Rod-01
Tungsten Alloy Swaging Rod for Military-02
Tungsten Alloy Military Swaging Rod

15.8 - 18.75 g/cm3, 20 - 35 Tungsten Alloy Swaging Rod for Military; Tungsten Alloy Rod Used In The FJFB-3 3-die Set

Contiguity and hardness variation in sintered, heat-treated and swaged tungsten alloy.

Tungsten Alloy Swaging Rod Main Properties for Military :

* High density
* High melting point
* Small volume
* Excellent hardness
* Superior wearing resistance
* High ultimate tensile strength
* High ductility
* High temperature resistance
* Low vapor pressure

Tungsten Alloy Swaging Rod

Military Application of Tungsten Alloy Swaging Rod

Tungsten alloy swaging rod can be used in military defense, such as depleted uranium kinetic energy penetrators, bullet, armor piercing, armor piercing bullets, sniper rifle penetrator, etc.
depleted uranium penetrator depleted uranium penetrator

Depleted Uranium Penetrator

Main Processing of Tungsten Alloy Swaging Rod:

1). Mixing
2). Pressing
3). Sintering
4). Heat treatment
5). Swaging
6). Machining
Repeated heat treatment and swaging is performed need at least several times.
In this way, tungsten alloy swaging rod can be improved at tensile strength as well decrease elongation and impact toughnes.

Tungsten Alloy Swaging Military Rod Properties Table

Composition

Processing

Density
g/cm3

Tensile strength
Min. Mpa

Elongation
Min. %

Hardness
Min. HRC

90WNiFe

Heat treatment

17.10±0.15

/

/

/

92.2WNiFe

Heat treatment

17.60±0.15

/

/

/

Swaging

/

/

/

91.7WNiFe

Heat treatment

17.65±0.15

/

/

/

93 WNiFe

Heat treatment

18.10±0.10

/

/

/

94 WNiFe

Heat treatment

17.90±0.10

/

/

/

95 WNiFe

Heat treatment

18.10±0.15

/

/

/

Swaging

/

/

/

96 WNiFe

Heat treatment

18.30±0.15

/

/

/

Swaging

/

/

/

97 WNiFe

Heat treatment

17.20±0.15

/

/

/

97 WNiFe

Heat treatment

17.65±0.15

/

/

/

97 WNiFe

Heat treatment

18.15±0.15

/

/

/

If you want to know more details about tungsten alloy military swaging rod, please feel free to contact us by email: sales@chinatungsten.com or call: 0086 592 5129696.
Related Links: What's Tungsten Alloy| Tungsten Heavy Alloy Grades| Tungsten Heavy Alloy Application
Address: 3F, No.25 WH Rd., Xiamen Software Park Ⅱ, FJ 361008,China
sales@chinatungsten.com sales@xiamentungsten.com
 Certified by MIIT:闽B2-20090025 闽ICP备06012101号-1
Copyright©1997 - 2016 ChinaTungsten Online All Rights Reserved