Mil-T-21014
Grade |
Mil-T-21014 |
Class1 |
Class 1 |
Class 2 |
Class 3 |
Class 3 |
Class 4 |
Composition |
90%W,
6%Ni4%Cu |
90%W,
7%Ni3%Fe |
92.5%W,
5.25%Ni
2.25%Fe |
95%W,
3.5%Ni
1.5% Cu |
95%W,
3.5%Ni
1.5%Fe |
97%W,
2.1%Ni
0.9%Fe |
Density (gm/cc;lbs/in3) |
17;0.614 |
17;0.614 |
17.5;0.632 |
18;0.65 |
18;0.65 |
18.5;0.668 |
Hardness (RC) |
24 |
25 |
26 |
27 |
27 |
28 |
Ultimate Tensile Strength (PSI) |
110,000 |
120,000 |
114,000 |
110,000 |
120,000 |
123,000 |
Yield Strength, .2% Offset (PSI) |
80,000 |
88,000 |
84,000 |
85,000 |
90,000 |
85,000 |
Elongation (% in 1″) |
6 |
10 |
7 |
7 |
7 |
5 |
Proportional Elastic Limit (PSI) |
45,000 |
52,000 |
46,000 |
45,000 |
44,000 |
45,000 |
Magnetic Properties |
Nil |
Slightly
Magnetic |
Slightly
Magnetic |
Nil |
Slightly
Magnetic |
Slightly
Magnetic |
ASTM-B-459-67 |
Grade1
Type Ⅱ && Ⅲ |
Grade1
Type Ⅱ && Ⅲ |
Grade2
Type Ⅱ && Ⅲ |
Grade3
Type Ⅱ && Ⅲ |
Grade3
Type Ⅱ && Ⅲ |
Grade4
Type Ⅱ && Ⅲ |
NAVY MIL-T-21014: tungsten base parts, high density metal (sintered or hot pressed), coated, electrodeposited chromium
ASTM B 777-99
Class |
1 |
2 |
3 |
4 |
Tungsten Nominal % |
90 |
92.5 |
95 |
97 |
Density (g/cc) |
16.85-17.25 |
17.15-17.85 |
17.75-18.35 |
18.25-18.85 |
Hardness (HRC) Max |
32 |
33 |
34 |
35 |
Ultimate Tensile Strength |
ksi |
110 |
110 |
105 |
100 |
Mpa |
758 |
758 |
724 |
689 |
Yield Strength at 0.2% off-set |
ksi |
75 |
75 |
75 |
75 |
Mpa |
517 |
517 |
517 |
517 |
Elongation, % |
5 |
5 |
3 |
2 |
ASTM B777-99 Standard Specification for Tungsten Base, High-Density Metal
1.his specification covers the requirements for four classes of machinable,high-density tungsten base metal produced by consolidation of metal powder mixtures of which the composition is mainly tungsten. This material specification may be used for bare parts or be used for parts that may be coated with other materials for protection against corrosion and abrasion.
2. Intended Use -Parts made from this material are intended for uses such as weights or counter-balances in static or dynamic balancing high-speed rotating inertia members, radiation shielding, hypervelocity impact, and vibration-damping applications.
3.Special Applications -For particular applications, properties or requirements may be important. These alloys may contain elements which make them magnetic. Where freedom from magnetic response is required, this should be specified in the purchase order. Class 4 is not available in a non-magnetic grade. For purposes of this specification, non-magnetic characteristics are defined as material having a maximum magnetic permeability of 1.05. Also for special applications involving large sections, methods for determining internal quality, such as mechanical tests on specimens from these larger sections or suitable nondestructive tests may be applied. If required, these additional tests shall be specified in the purchase order.
|