Mil-T-21014
等级 |
Mil-T-21014 |
Class1 |
Class 1 |
Class 2 |
Class 3 |
Class 3 |
Class 4 |
配比 |
90%W,
6%Ni4%Cu |
90%W,
7%Ni3%Fe |
92.5%W,
5.25%Ni
2.25%Fe |
95%W,
3.5%Ni
1.5% Cu |
95%W,
3.5%Ni
1.5%Fe |
97%W,
2.1%Ni
0.9%Fe |
密度 (gm/cc;lbs/in3) |
17;0.614 |
17;0.614 |
17.5;0.632 |
18;0.65 |
18;0.65 |
18.5;0.668 |
硬度 (RC) |
24 |
25 |
26 |
27 |
27 |
28 |
极限抗拉强度 (PSI) |
110,000 |
120,000 |
114,000 |
110,000 |
120,000 |
123,000 |
屈服强度, .2% Offset (PSI)
|
80,000 |
88,000 |
84,000 |
85,000 |
90,000 |
85,000 |
延伸率(% in 1″) |
6 |
10 |
7 |
7 |
7 |
5 |
比例弹性限度 (PSI) |
45,000 |
52,000 |
46,000 |
45,000 |
44,000 |
45,000 |
|
磁性 |
Nil |
Slightly
Magnetic |
Slightly
Magnetic |
Nil |
Slightly
Magnetic |
Slightly
Magnetic |
ASTM-B-459-67 |
Grade1
Type Ⅱ && Ⅲ |
Grade1
Type Ⅱ && Ⅲ |
Grade2
Type Ⅱ && Ⅲ |
Grade3
Type Ⅱ && Ⅲ |
Grade3
Type Ⅱ && Ⅲ |
Grade4
Type Ⅱ && Ⅲ |
NAVY MIL-T-21014:钨基零件, 高比重金属 (烧结或热压), 镀层, 电镀铬
ASTM B 777-99
Class |
1 |
2 |
3 |
4 |
钨比例 % |
90 |
92.5 |
95 |
97 |
密度(g/cc) |
16.85-17.25 |
17.15-17.85 |
17.75-18.35 |
18.25-18.85 |
硬度 (HRC) Max
|
32 |
33 |
34 |
35 |
极限抗拉强度 |
ksi |
110 |
110 |
105 |
100 |
Mpa |
758 |
758 |
724 |
689 |
屈服强度 at 0.2% off-set |
ksi |
75 |
75 |
75 |
75 |
Mpa |
517 |
517 |
517 |
517 |
延伸率, % |
5 |
5 |
3 |
2 |
钨基，高比重金属的ASTM B777-99标准
1.规格包括了四种等级，易加工，高比重钨基金属，由金属粉末混合压制而成，而主要成分为钨。这种材料的规格可以用来做零部件或者有其他镀层来保护不受腐蚀。
2.用途 -此材料制成的产品可用来做静态动态高速惯性系统的配重，屏蔽件，减震产品。
3.特殊用途 -如用于特殊用途, 性能要求就很重要.
此合金包括可以使其有磁性的材料。若要求不含磁，必须在订单中指明。Class 4不是无磁等级.
此项规格，无磁性被定义为最大磁导率为1.05.
|