Mil-T-21014
等級 |
Mil-T-21014 |
Class1 |
Class 1 |
Class 2 |
Class 3 |
Class 3 |
Class 4 |
配比 |
90%W,
6%Ni4%Cu |
90%W,
7%Ni3%Fe |
92.5%W,
5.25%Ni
2.25%Fe |
95%W,
3.5%Ni
1.5% Cu |
95%W,
3.5%Ni
1.5%Fe |
97%W,
2.1%Ni
0.9%Fe |
密度 (gm/cc;lbs/in3) |
17;0.614 |
17;0.614 |
17.5;0.632 |
18;0.65 |
18;0.65 |
18.5;0.668 |
硬度 (RC) |
24 |
25 |
26 |
27 |
27 |
28 |
極限抗拉強度 (PSI) |
110,000 |
120,000 |
114,000 |
110,000 |
120,000 |
123,000 |
屈服強度, .2% Offset (PSI)
|
80,000 |
88,000 |
84,000 |
85,000 |
90,000 |
85,000 |
延伸率(% in 1″) |
6 |
10 |
7 |
7 |
7 |
5 |
比例彈性限度 (PSI) |
45,000 |
52,000 |
46,000 |
45,000 |
44,000 |
45,000 |
|
磁性 |
Nil |
Slightly
Magnetic |
Slightly
Magnetic |
Nil |
Slightly
Magnetic |
Slightly
Magnetic |
ASTM-B-459-67 |
Grade1
Type Ⅱ && Ⅲ |
Grade1
Type Ⅱ && Ⅲ |
Grade2
Type Ⅱ && Ⅲ |
Grade3
Type Ⅱ && Ⅲ |
Grade3
Type Ⅱ && Ⅲ |
Grade4
Type Ⅱ && Ⅲ |
NAVY MIL-T-21014:鎢基零件, 高比重金屬 (燒結或熱壓), 鍍層, 電鍍鉻
ASTM B 777-99
Class |
1 |
2 |
3 |
4 |
鎢比例 % |
90 |
92.5 |
95 |
97 |
密度(g/cc) |
16.85-17.25 |
17.15-17.85 |
17.75-18.35 |
18.25-18.85 |
硬度 (HRC) Max
|
32 |
33 |
34 |
35 |
極限抗拉強度 |
ksi |
110 |
110 |
105 |
100 |
Mpa |
758 |
758 |
724 |
689 |
屈服強度 at 0.2% off-set |
ksi |
75 |
75 |
75 |
75 |
Mpa |
517 |
517 |
517 |
517 |
延伸率, % |
5 |
5 |
3 |
2 |
鎢基，高比重金屬的ASTM B777-99標準
1.規格包括了四種等級，易加工，高比重鎢基金屬，由金屬粉末混合壓制而成，而主要成分為鎢。這種材料的規格可以用來做零部件或者有其他鍍層來保護不受腐蝕。
2.用途 -此材料制成的產品可用來做靜態動態高速慣性系統的配重，屏蔽件，減震產品。
3.特殊用途 -如用于特殊用途, 性能要求就很重要.
此合金包括可以使其有磁性的材料。若要求不含磁，必須在訂單中指明。Class 4不是無磁等級.
此項規格，無磁性被定義為最大磁導率為1.05.
|